Semiconductor laser device, semiconductor laser system, optical pickup module and manufacturing for semiconductor laser system

ABSTRACT

A semiconductor laser device comprises an n − type cladding layer  103  made of n − type Al 0.3 Ga 0.7 ) 0.5 In 0.5 P, an undoped active layer  104  and a first p-type cladding layer  105  made of p − type (Al 0.3 Ga 0.7 ) 0.5 In 0.5 P. These layers are successively stacked in bottom-to-top order. The active layer  104  has a multi-quantum well structure composed of a first optical guide layer of undoped Al 0.4 Ga 0.6 As, a layered structure in which well layers of undoped GaAs and barrier layers of undoped Al 0.4 Ga 0.6 As are alternately formed, and a second optical guide layer of undoped Al 0.4 Ga 0.6 As. The first optical guide layer, the layered structure and the second optical guide layer are successively stacked in bottom-to-top order.

BACKGROUND OF THE INVENTION

(1) Field of the Invention

The present invention relates to an optical pickup module, asemiconductor laser device and a semiconductor laser system bothincorporated into the optical pickup module, and a method formanufacturing a semiconductor laser system.

(2) Description of Related Art

In recent years, the widespread use of optical disk systems has advancedthe increase of the recording density of an optical disk. The opticaldisk systems have been demanded not only to reproduce data from CDs butalso to reproduce data from and record data in write-once CDs (CD-Rs).

By the way, a red laser with a wavelength of a 650 nm band is used toreproduce data from DVDs, and an infrared laser with a wavelength of a780 nm band is used to reproduce data from and record data in CDs orCD-Rs.

Accordingly, at present, systems for reproducing data from and recordingdata in DVDs and CDs (RAMBO systems) each require two laser devices ofred and infrared semiconductor laser devices and optical componentscorresponding to the laser devices.

On the other hand, with size reduction of notebook computers or thelike, the RAMBO systems have been demanded to become more compact.Therefore, optical pickup modules need become more compact.

To cope with this, a monolithic two-wavelength semiconductor lasersystem is suggested which is obtained by integrating a red semiconductorlaser device and an infrared semiconductor laser device. In thetwo-wavelength semiconductor laser system, the integration of the twosemiconductor laser devices allows the shared use of an optical systemand data reproduction and recording with a single optical component.Therefore, optical pickup modules can be made more compact and thinner.

However, crystal growth must be carried out many times to fabricate amonolithic two-wavelength semiconductor laser system obtained byintegrating a red semiconductor laser device and an infraredsemiconductor laser device on a single substrate. Thus, the number ofprocess steps increases, leading to increased cost.

In order to reduce cost, it is desired that the number of crystalgrowths is as small as possible. For that purpose, it is preferable thatan infrared laser device structure serves as a basis for a semiconductorlaser system and a red laser device structure is added to the infraredlaser device structure.

However, it is generally difficult to fabricate a red semiconductorlaser device made of a material other than AlGaInP-based materials.Hence, it should be considered that a red semiconductor laser device isinevitably made of an AlGaInP-based material.

Thus, an infrared semiconductor laser device need be made of a materialthat can be grown while being lattice-matched to the AlGaInP-basedmaterial.

An infrared semiconductor laser device is typically made of GaAs orAlGaAs that is a material containing As. However, a part of itsstructure can be made of a material containing Phosphorus (P), such asan AlGaInP-based material, instead of GaAs or AlGaAs, to fabricate aninfrared semiconductor laser device. The use of an AlGaInP-basedmaterial for an infrared semiconductor laser device permits thesimultaneous crystal growths of layers necessary for a red semiconductorlaser device and an infrared semiconductor laser device. This does notlead to increase in the number of process steps in fabricating amonolithic two-wavelength semiconductor laser system. Thus, the use ofan AlGaInP-based material for an infrared semiconductor is useful forcost reduction. In particular, the use of an infrared semiconductorlaser device using a material containing P for cladding layerssuppresses the overflow of carriers as compared with the use of claddinglayers made of a material containing arsenic (As), thereby obtainingexcellent temperature characteristics. Therefore, stable characteristicscan be obtained even in a hostile environment such as an environmentsurrounding a vehicle-mounted infrared semiconductor laser device.

In relation to infrared semiconductor laser devices using a materialcontaining P for cladding layers, there are suggested structures andfabrication methods as disclosed in Japanese Unexamined PatentPublication No. 5-218582 (hereinafter, referred to as Document 1),Japanese Unexamined Patent Publication No. 2001-57462 (hereinafter,referred to as Document 2), and Japanese Unexamined Patent PublicationNo. 2002-111136 (hereinafter, referred to as Document 3).

Infrared semiconductor laser devices having cladding layers made of amaterial containing P as disclosed in Documents 1 and 2 are eachfabricated on a single-crystal substrate by successively growing thecrystals of a cladding layer of a first conductive type, an active layerand a cladding layer of a second conductive type.

However, in the infrared semiconductor laser devices, a GaAs-based orAlGaAs-based material need be used for an active layer because of adesired emission wavelength. In this case, it is difficult to obtainexcellent crystallinity on the interface between a cladding layer madeof a material containing P and an active layer made of a materialcontaining As.

FIG. 13 illustrates an energy band diagram of a known infraredsemiconductor laser device having cladding layers made of a materialcontaining P. As seen from FIG. 13, the energy difference between eachcladding layer and the optical guide layer contacting the cladding layeris secured, because the optical guide layer is also composed of amaterial containing phosphorus (P), specifically, GaInP.

By the way, in an actual fabrication process, a cladding layer, anoptical guide layer and an active layer are typically successively grownby metal organic chemical vapor deposition (hereinafter, referred to asMOCVD) or the like. When the cladding layers and the optical guidelayers are formed of a material containing P, the source gas need beswitched from a gas containing P to a gas containing As in growing awell layer constituting the active layer.

In this case, the gas containing P and the gas containing As coexist ina reactor. This causes a loss of the steepness of composition change orthe like at the interfaces between the optical guide layers and theactive layers. Therefore, the following problems occur: an injectioncurrent becomes uneven; and a multi-quantum well layer has a longerwavelength than the designed wavelength and thus emission intensitybecomes extremely feeble.

The active layer determines the characteristics of the semiconductorlaser element, such as wavelength and lifetime, and is thereforerequired to have excellent crystallinity.

However, it turned out that when a cladding layer made of(Al_(0.5)Ga_(0.5))_(0.5)In_(0.5)P is grown on the substrate and then amulti-quantum well layer made of GaAs/(Al_(0.5)Ga_(0.5))_(0.5)In_(0.5)Pis grown on the cladding layer, the substrate surface is whitened andtherefore the designed wavelength cannot be obtained.

It is considered that the reason for this is that since themulti-quantum well layer was grown with a gas containing P and a gascontaining As mixed, its epitaxial growth has been done unsuccessfully.When the crystallinity of the active layer is thus impaired due to across contamination in switching the source gas, the device reliabilitydecreases in lifetime and resistance regardless of the obtainment of thedesigned wavelength.

Document 3 discloses an example in which an AlGaAs-based optical guidelayer is placed between an AlGaInP-based cladding layer and an activelayer. In this case, a multi-quantum well layer has a layered structurecomposed of a well layer made of Al_(x)Ga_(1−x)As (x≦0.15) and a barrierlayer made of In_(0.5)(Ga_(1−x)Al_(z))_(0.5)P (0≦z≦0.2). Therefore, thesource gas need be switched from a gas containing P to a gas containingAs. Hence, the problem that excellent crystals cannot be obtained is notsolved.

SUMMARY OF THE INVENTION

In view of the above, an object of the present invention is to improvethe reliability of an infrared semiconductor laser device comprisingcladding layers of a material containing phosphorus (P) and an activelayer containing arsenic (As) but containing no phosphorus (P).

In order to attain the above object, a semiconductor laser device of thepresent invention comprises a cladding layer of a first conductive type,an active layer and a cladding layer of a second conductive type, saidlayers being stacked on a semiconductor substrate of the firstconductive type in bottom-to-top order, wherein the active layercomprises a layered structure composed of at least one pair of a welllayer and a barrier layer, an upper semiconductor layer formed on top ofthe layered structure, and a lower semiconductor layer formed beneaththe layered structure, the cladding layer of the first conductive typeand the cladding layer of the second conductive type are made of amaterial containing phosphorus, and the at least one pair of the welllayer and barrier layer and the lower semiconductor layer are made of amaterial that contains arsenic but does not substantially containphosphorus.

Herein, a material that does not substantially contain phosphorus meansthat even if a film formed by growth contains phosphorus, thisphosphorus is contained due to cross contamination in a growth device,i.e., phosphorus is not intentionally contained in a crystal.

According to the semiconductor laser device of the present invention,since the at least one pair of a well layer and a barrier layerconstituting the active layer are made of a material that containsarsenic but does not substantially contain phosphorus, the active layercan emit infrared light. The lower semiconductor layer is formed belowthe layered structure composed of at least one pair of a well layer anda barrier layer and is made of a material that contains arsenic but doesnot substantially contain phosphorus. Therefore, when the layeredstructure composed of at least one pair of a well layer and a barrierlayer is grown after the growth of the lower semiconductor layer, thesource gas need not be switched between a gas containing arsenic and agas containing phosphorus. Since a problem of contamination associatedwith the switching of the source gas is not thus caused, the layeredstructure constituting the active layer can have excellentcrystallinity. This can improve the characteristics and reliability ofan infrared semiconductor laser device having cladding layers made of amaterial containing phosphorus and an active layer that contains arsenicbut contain no phosphorus.

In the semiconductor laser device of the present invention, the uppersemiconductor layer is preferably made of a material that containsarsenic but does not substantially contain phosphorus.

In the semiconductor laser device of the present invention, the upperand lower semiconductor layers are preferably optical guide layers.

When the upper and lower semiconductor layers are optical guide layers,the band gap of each optical guide layer is equivalent to or larger thanthat of the well layer.

When the upper and lower semiconductor layers are optical guide layers,it is preferable that the cladding layer of the first conductive typeand the cladding layer of the second conductive type are made of(Al_(x)Ga_(1−x))_(y)In_(1−y)P (where 0≦x≦1 and 0≦y≦1) and the opticalguide layers are made of Al_(x)Ga_(1−x)As (where 0≦x≦1).

In this case, it is preferable that the well layer is made ofAl_(x)Ga_(1−x)As (where 0≦x≦1) and the barrier layer is made ofAl_(x)Ga_(1−x)As (where 0≦x≦1).

Furthermore, in this case, the well layer is preferably made ofAl_(x)Ga_(1−x)As (where 0≦x≦0.2).

Moreover, in this case, the optical guide layers are preferably made ofAl_(x)Ga_(1−x)As (where 0.4≦x≦1).

When the upper and lower semiconductor layers are optical guide layers,it is preferable that the optical guide layers each have a thickness of10 nm or more.

A semiconductor laser system of the present invention comprises aplurality of semiconductor laser devices for emitting light beams ofdifferent wavelengths, said plurality of semiconductor laser devicesbeing formed on a single substrate, wherein at least one of theplurality of semiconductor laser devices is any semiconductor laserdevice of the present invention.

The semiconductor laser device of the present invention can improve thecharacteristics and reliability of an infrared semiconductor laserdevice that constitutes a multi-wavelength semiconductor laser systemcomprising semiconductor laser devices for emitting light beams of aplurality of different wavelengths.

A first optical pickup module of the present invention comprises: anysemiconductor laser device of the present invention; and a lightreceiving unit for receiving light reflected from a recording mediumafter being emitted from the semiconductor laser device.

The first optical pickup module of the present invention can improve thecharacteristics and reliability of an infrared semiconductor laserdevice serving as a light source.

A second optical pickup module of the present invention comprises: asemiconductor laser system of the present invention; and a lightreceiving unit for receiving light reflected from a recording mediumafter being emitted from the semiconductor laser system.

The second optical pickup module of the present invention can improvethe characteristics and reliability of an infrared semiconductor laserdevice that constitutes a multi-wavelength semiconductor laser systemserving as a light source.

A method for manufacturing a semiconductor laser system of the presentinvention comprises the steps of: forming a first double-heterojunctionstructure on a semiconductor substrate; removing a predetermined regionof the first double-heterojunction structure to form a firstsemiconductor laser device of the remaining first double-heterojunctionstructure; forming a second double-heterojunction structure on thesemiconductor substrate including the top surface of the remaining firstdouble-heterojunction structure; and removing a region of the seconddouble-heterojunction structure located on the remaining firstdouble-heterojunction structure to form a second semiconductor laserdevice of the remaining second double-heterojunction structure, whereinthe step of forming a first double-heterojunction structure comprisesthe steps of: forming a first cladding layer made of a materialcontaining phosphorus on the semiconductor substrate; forming, on thefirst cladding layer, a lower semiconductor layer made of a materialthat contains arsenic but does not substantially contain phosphorus,then forming, on the lower semiconductor layer, a layered structure madeof a material that contains arsenic but does not substantially containphosphorus and composed of at least one pair of a well layer and abarrier layer, and then forming an upper semiconductor layer on thelayered structure, thereby forming a first active layer composed of thelower semiconductor layer, the layered structure and the uppersemiconductor layer; and forming, on the first active layer, a secondcladding layer made of a material containing phosphorus, and the step offorming a second double-heterojunction structure comprises the steps of:forming a third cladding layer made of a material containing phosphoruson the semiconductor substrate including the top surface of the firstsemiconductor laser device; forming a second active layer on the thirdcladding layer; and forming a fourth cladding layer on the second activelayer.

According to the method for manufacturing a semiconductor laser deviceof the present invention, the lower semiconductor layer that containsarsenic but does not substantially contain phosphorus is formed on thefirst cladding layer made of a material containing phosphorus.Thereafter, the layered structure is formed on the lower semiconductorlayer. The layered structure is made of a material that contains arsenicbut does not substantially contain phosphorus and constitutes the firstactive layer. Therefore, when the layered structure constituting thefirst active layer is grown after the growth of the lower semiconductorlayer, the source gas need not be switched between a gas containingarsenic and a gas containing phosphorus. Since a problem ofcontamination associated with the switching of the source gas is notthus caused, the layered structure constituting the first active layercan have excellent crystallinity. This can improve the characteristicsand reliability of a first semiconductor laser device of a firstdouble-heterojunction structure.

In the method for manufacturing a semiconductor laser system, the stepof forming a first double-heterojunction structure preferably comprisesthe step of continuously growing the first cladding layer, the firstactive layer and the second cladding layer.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view illustrating the structure of asemiconductor laser device according to a first embodiment of thepresent invention.

FIG. 2 is a cross-sectional view illustrating the structure of an activelayer of the semiconductor laser device according to the firstembodiment of the present invention.

FIG. 3 is an energy band diagram of the semiconductor laser deviceaccording to the first embodiment of the present invention.

FIG. 4 is a cross-sectional view illustrating a semiconductor layeredstructure used to measure the photoluminescence (hereinafter, referredto as PL) of the semiconductor laser device according to the firstembodiment of the present invention.

FIG. 5 is a graph illustrating variations in PL peak intensity of thesemiconductor layered structure used to measure the PL of thesemiconductor laser device according to the first embodiment of thepresent invention with the change in the thickness of an optical guidelayer.

FIG. 6 is a graph illustrating the relationship between the PLwavelength and intensity of the semiconductor layered structure used tomeasure the PL of the semiconductor laser device according to the firstembodiment of the present invention when the thickness of the opticalguide layer is 7 or 10 nm.

FIG. 7A is a graph illustrating the current-light output characteristicsof a known semiconductor laser device.

FIG. 7B is a graph illustrating the current-light output characteristicsof the semiconductor laser device according to the first embodiment.

FIG. 8 is a cross-sectional view illustrating the structure of atwo-wavelength semiconductor laser system according to a secondembodiment of the present invention.

FIG. 9 is a cross-sectional view illustrating the structure of a redlaser active layer of the two-wavelength semiconductor laser systemaccording to the second embodiment of the present invention.

FIGS. 10A through 10C are cross-sectional views showing process steps ina method for manufacturing a two-wavelength semiconductor laser systemaccording to the second embodiment of the present invention.

FIGS. 11A through 11C are cross-sectional views showing the otherprocess steps in the method for manufacturing a two-wavelengthsemiconductor laser system according to the second embodiment.

FIG. 12 is a schematic diagram illustrating the structure of an opticalpickup module according to a third embodiment of the present invention.

FIG. 13 is an energy band diagram of a known infrared semiconductorlaser device.

DETAILED DESCRIPTION OF THE INVENTION

(Embodiment 1)

A description will be given below of a semiconductor laser deviceaccording to a first embodiment of the present invention with referenceto FIGS. 1 through 7.

FIG. 1 illustrates the structure of an infrared semiconductor laserdevice according to the first embodiment. As shown in FIG. 1, a bufferlayer 102 of n⁻type GaAs (Si doping amount: 1.0×10¹⁸ cm⁻3) is formed ona substrate 101 of n⁻type GaAs (Si doping amount:

1.0×10¹⁸ cm⁻3). The buffer layer 102 is formed thereon to allow ann⁻type cladding layer 103 that will be described later to have excellentcrystallinity.

A double-heterojunction structure is formed on the buffer layer 102. Thedouble heterojunction structure is composed of an n⁻type cladding layer103 of n⁻type (Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P (Si doping amount:1.0×10 ¹⁸ cm⁻3), an undoped active layer 104, a first p-type claddinglayer 105 of p⁻type (Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P (Zn doping amount:3×10¹⁷cm⁻3), an etching stopper layer 106 of p⁻type Ga_(0.5)In_(0.5)P(Zn doping amount: 1×10¹⁸ cm⁻3), a second p-type cladding layer 107 ofp⁻type (Al_(0.3)Ga_(0.7))_(0.5)I)_(0.5)In (Zn doping amount: 1×10¹⁸cm⁻3), and a contact layer 110 of p⁻type GaAs (Zn doping amount: 3×10¹⁸cm⁻3). These layers are successively stacked in bottom-to-top order.

The second p-type cladding layer 107 is processed to take the form of astripe-shaped ridge. A cap layer 108 of p⁻type Ga_(0.5)In_(0.5)P (Zndoping amount: 2×10¹⁸cm⁻3) is formed on the second p⁻type cladding layer107.

FIG. 2 illustrates the structure of the active layer 104. As shown inFIG. 2, the active layer 104 has a multi-quantum well structure composedof a first optical guide layer 104 a of undoped Al_(0.4)Ga_(0.6)As, alayered structure in which four well layers 104 b of undoped GaAs andthree barrier layers 104 c of undoped Al_(0.4)Ga_(0.6)As are alternatelystacked, and a second optical guide layer 104 d of undopedAl_(0.4)Ga_(0.6)As. The first optical guide layer 104 a, the layeredstructure and the second optical guide layer 104 d are successivelystacked in bottom-to-top order.

The thicknesses of the first and second optical guide layers 104 a and104 d are each preferably 10 nm or more. The reason for this will bedescribed later.

There are considerations in determining the In, Ga and Al contents inthe n-type cladding layer 103, the active layer 104, the first p-typecladding layer 105, the etching stopper layer 106, a second p-typecladding layer 107, and the cap layer 108, which constitute thedouble-heterojunction structure. These considerations are that eachlayer (103, 104, 105, 106, 107, 108) is substantially equivalent inlattice constant to the substrate 101, and that each of the n-typecladding layer 103 and the first p-type cladding layer 105 has band gapenergy larger than that of the active layer 104.

A current blocking layer 109 of n⁻type Al_(0.5)In_(0.5)P (Si dopingamount: 1.0×10¹⁸ cm⁻3) is formed on both sides of the second p-typecladding layer 107, and the contact layer 110 of p⁻type GaAs (Zn dopingamount: 7×10¹⁸ cm⁻3) is formed on the cap layer 108 and the currentblocking layer 109.

A p-side electrode 111 is formed on the top surface of the contact layer110, and an n-side electrode 112 is formed on the bottom surface of thesubstrate 101.

Furthermore, the layers other than the p-side and n-side electrodes 111and 112 are all formed by a crystal growth method using MOCVD.

A light wave is guided by the first p-type cladding layer 105 and thesecond p-type cladding layer 107 processed to take the form of astripe-shaped ridge.

The n-type cladding layer 103 has a thickness of 1.5 μm, the activelayer 104 has a thickness of 50 nm, and the first and second opticalguide layers 104 a and 104 d constituting the active layer 104 each havea thickness of 10 nm. The first p-type cladding layer 105 and theridge-shaped second p-type cladding layer 107 each have a thickness of0.85 μm, and the etching stopper layer 106 has a thickness of 10 nm. Theridge-shaped second p-type cladding layer 107 has a width of 3.5 μm atthe ridge top.

FIG. 3 illustrates an energy band diagram of an infrared semiconductorlaser device according to the first embodiment. As seen from FIG. 3, theinterfaces between the layers made of a material containing P and thelayers made of a material containing As (P-As interfaces) shift from theinterfaces between the well layers and the optical guide layers to theinterfaces between the optical guide layers and the cladding layers.

A description will be given below of the effects produced by the factthat the P-As interfaces move from the interfaces between the well layerand the optical guide layers to the interfaces between the optical guidelayers and the cladding layers.

As described above, in order to fabricate an infrared semiconductorlaser device with a wavelength of a 780 nm band using a materialcontaining P, the source gas need be switched from a material containingP (cladding layer) to a material containing As (active layer).

FIG. 4 is a cross-sectional view illustrating a semiconductor layeredstructure for measuring photoluminescence (hereinafter, referred to asPL) according to the first embodiment.

The semiconductor layered structure is formed in the following manner. Abuffer layer 12 of n⁻type GaAs and an undoped first cladding layer (itsthickness: 0.5 μm) 13 of (Al_(0.5)Ga_(0.5))_(0.5)In_(0.5)P aresuccessively grown on a substrate 11 of n⁻type GaAs. Thereafter, a firstoptical guide layer 14 of Al_(0.4)Ga_(0.6)As, a layered structure inwhich four well layers 15 of GaAs and three barrier layers 16 ofAl_(0.4)Ga_(0.6)As are alternately stacked, and a second optical guidelayer 17 of Al_(0.4)Ga_(0.6)As are grown on the first cladding layer 13.Then, an undoped second cladding layer (its thickness: 0.15 μm) 18 of(Al_(0.5)Ga_(0.5))_(0.5)In_(0.5)P is grown on the second optical guidelayer 17.

FIG. 5 illustrates variations in the PL peak intensity of thesemiconductor layered structure shown in FIG. 4 with the change in thethicknesses of the first and second optical guide layers 14 and 17. Itis seen from FIG. 5 that with the increasing thickness of each of thefirst and second optical guide layers 14 and 17, the PL peak intensityis increasing. This indirectly means that the crystallinity of theactive layer becomes better with the increasing thickness of each of thefirst and second optical guide layers 14 and 17. Furthermore, when thefirst and second optical guide layers 14 and 17 each have a thickness of10 nm or more, the intensity of a PL peak wavelength is saturated. Thisrepresents that an active layer whose interfaces have excellentsteepness is fabricated within the range in which the first and secondoptical guide layers 14 and 17 each have a thickness of 10 nm or more.

FIG. 6 illustrates the correlation between the PL wavelength andintensity of the semiconductor layered structure shown in FIG. 4 whenthe first and second optical guide layers 14 and 17 each have athickness of 7 nm or 10 nm. As seen from FIG. 6, when the first andsecond optical guide layers 14 and 17 each have a thickness of 7 nm, theintensity of the PL wavelength is smaller as compared with when theyeach have a thickness of 10 nm, and the peak wavelength is shifted to alonger wavelength side in spite of the same quantum well structure.

The reason for this is considered as follows. When the first opticalguide layer 14 has a small thickness, the crystallinity of the firstoptical guide layer 14 is degraded due to the influence of contaminationwith P from the source gas containing P in the formation of the firstcladding layer 13 and a quantum well layer is grown on the first opticalguide layer 14 having degraded crystallinity. On the other hand, whenthe first optical guide layer 14 has a larger thickness, a part of thefirst optical guide layer 14 that is not affected by P contamination hasa larger thickness and thus the crystallinity of the part is recovered.This also provides an excellent crystallinity of the quantum well layergrown on the first optical guide layer 14 and thus stablecharacteristics of the active layer.

It is seen from the above descriptions based on FIGS. 5 and 6 that whenthe first and second optical guide layers 14 and 17 each have athickness of 10 nm or more, this provides an excellent crystallinity ofthe active layer.

As described above, according to the semiconductor laser device of thefirst embodiment, the infrared semiconductor laser having claddinglayers made of a material containing P can suppress the influence of Pcontamination in the crystal growth of the optical guide layer. Thus,the semiconductor laser device can have stable characteristics and highreliability. Furthermore, since the source gas can be switched in thesame reactor, the crystal growth of each layer can successively becarried out. This can reduce facilities necessary for the film formationand improve throughput.

The energy bands of optical guide layers will be described hereinafter.

Document 1 discloses the following problem. If the band gap differencebetween each of cladding layers made of AlGaInP and an active layer madeof GaAs is large, a large band discontinuity is present in a valenceband. This causes a hetero-spike, which interferes with hole injection.In a semiconductor laser device of Document 1, optical guide layers ofGaInP are provided between cladding layers and the corresponding welllayers, thereby reducing the band discontinuity.

On the other hand, according to the first embodiment, the band gapbetween each of the n-type cladding layer 103 and the first p-typecladding layer 105 and the well layer 104 b can gently be changed byadjusting the Al contents of the first and second optical guide layers104 a and 104 d. More particularly, if the compositions of the first andsecond optical guide layers 104 a and 104 b are each set toAl_(x)Ga_(1−x)As (x=0.4) as in the first embodiment, the first andsecond optical guide layers 104 a and 104 d can have the same band gapas the optical guide layers of GaInP disclosed in Document 1. If the Alcontent x is 0.4 or more, the energy band is substantially continuousand injection current becomes uniform.

Since in the first embodiment the first and second optical guide layers104 a and 104 d each have a thickness of 10 nm or more, holes are movedsmoothly, which are injected through the first and second optical guidelayers 104 a and 104 d into the well layers 104 b. Thus, the aboveproblem concerning the hetero-spike is solved. Furthermore, Zn can berestrained from being diffused from the first p-type cladding layer 105into the active layer 104. This prevents the active layer 104 from beingdegraded in its crystallinity during a reliability test.

FIG. 7A illustrates the current-light output characteristics (I-Lcharacteristics) of a known semiconductor laser device having claddinglayers made of AlGaAs. FIG. 7B illustrates the current-light outputcharacteristics of the semiconductor laser device of the firstembodiment having cladding layers made of AlGaInP. As seen fromcomparison between FIGS. 7A and 7B, the semiconductor laser device ofthe first embodiment can bear comparison in characteristics with theknown semiconductor laser device having cladding layers made of aGaAs-based material.

Moreover, the semiconductor laser device of the first embodiment canensure a large band gap difference between each of the n-type claddinglayer 103 and the first p-type cladding layer 105 and the active layer104. This can suppress the overflow of carriers and reduce reactivecurrent.

The actual test on the semiconductor laser device has shown that theoperating characteristics do not vary until a temperature ofapproximately 200° C. This means that the semiconductor laser device ofthe first embodiment of the present invention is suitable for operationsin motor vehicles or in hostile environments.

The orientation of the principal surface of the substrate 101 isinclined about 10 degrees from (100) in the [011] or [0-11] direction.The reason for this is that a natural superlattice is restrained fromgrowing during the growth of the AlGaInP layer and thus the AlGaInPlayer can precisely be controlled to have a desired composition.

(Embodiment 2)

A description will be given of a two-wavelength semiconductor lasersystem and a method for manufacturing the same according to a secondembodiment of the present invention with reference to FIGS. 8, 9 and 10Athrough 11C.

FIG. 8 illustrates the structure of a monolithic two-wavelengthsemiconductor laser system in which an infrared laser device A and a redlaser device B are formed on the same substrate. The infrared laserdevice A emits a light beam with a wavelength of a 780 nm band, and thered laser device B emits a light beam with a wavelength of a 650 nmband. The infrared laser device A is separated from the red laser deviceB by an isolation trench C reaching the substrate.

The structure of the infrared laser device A will be describedhereinafter.

Stacked on a substrate 201 of n⁻type GaAs in bottom-to-top order are abuffer layer 202 of n⁻type GaAs (Si doping amount: 1.0×10¹⁸ cm⁻3), ann-type cladding layer 203 of n⁻type (Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P(Si doping amount: 1.0×10¹⁸ cm⁻3), an undoped infrared active layer 204,a first p-type cladding layer 205 of p⁻type(Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P (Zn doping amount: 3×10¹⁷ cm⁻3), anetching stopper layer 206 of p⁻type Ga_(0.5)In_(0.5)P (Zn doping amount:1×10¹⁸ cm⁻3), a second p-type cladding layer 207 of p⁻type(Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P (Zn doping amount: 1×10¹⁸ cm⁻3), and acap layer 208 of p⁻type Ga_(0.5)In_(0.5)P. The buffer layer 202 isformed on the substrate 201 to allow the n-type cladding layer 203 tohave excellent crystallinity. The infrared active layer 204 has the samestructure as that described in the first embodiment with reference toFIG. 2.

The second p-type cladding layer 207 is processed to take the form of astripe-shaped ridge, and the stripe-shaped cap layer 208 is formed onthe second p-type cladding layer 207. A current blocking layer 209 ofn⁻type Al_(0.5)In_(0.5)P (Si doping amount: 1.0×10¹⁸ cm⁻3) is formed onboth sides of the second p-type cladding layer 207, and a contact layer210 of p⁻type GaAs (Zn doping amount: 7×10¹⁸ cm⁻3) is formed on the caplayer 208 and the current blocking layer 209.

A p-side electrode 211 is formed on the top surface of the contact layer210, and an n-side electrode 215 is formed on the bottom surface of thesubstrate 201.

The structure of the red laser device B will be described hereinafter.

Stacked on the substrate 201 in bottom-to-top order are a buffer layer222 of n⁻type GaAs (Si doping amount: 1.0×10¹⁸ cm⁻3), an n-type claddinglayer 223 of n⁻type (Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P (Si doping amount:1.0×10¹⁸ cm⁻3), an undoped red active layer 224, a first p-type claddinglayer 225 of p⁻type (Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P (Zn doping amount:5×10¹⁷ cm⁻3), an etching stopper layer 226 of p⁻type Ga_(0.5)In_(0.5)P(Zn doping amount: 1×10¹⁸ cm⁻³), a second p-type cladding layer 227 ofp⁻type (Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P (Zn doping amount: 1×10¹⁸cm⁻3), and a cap layer 228 of p⁻type Ga_(0.5)In_(0.5)P. The buffer layer222 is formed on the substrate 201 to allow the n-type cladding layer223 to have excellent crystallinity.

The second p-type cladding layer 227 is processed to take the form of astripe-shaped ridge, and the stripe-shaped cap layer 228 is formed onthe second p-type cladding layer 227. A current blocking layer 229 of ntype Al_(0.5)In_(0.5)P (Si doping amount: 1.0×10¹⁸ cm⁻3) is formed onboth sides of the second p-type cladding layer 227, and a contact layer230 of p⁻type GaAs (Zn doping amount: 7×10¹⁸ cm⁻3) is formed on the caplayer 228 and the current blocking layer 229.

A p-side electrode 231 is formed on the top surface of the contact layer230.

FIG. 9 illustrates the structure of the red active layer 224. As shownin FIG. 9, the red active layer 224 has a multi-quantum well structurecomposed of a first optical guide layer 224 a of undoped(Al_(0.5)Ga_(0.5))_(0.5)In_(0.5)P, a layered structure in which fourwell layers 224 b of undoped Ga_(0.5)In_(0.5)P and three barrier layers224 c of undoped (Al_(0.5)Ga_(0.5))_(0.5)In_(0.5)P are alternatelystacked, and a second optical guide layer 224 d of undoped(Al_(0.5)Ga_(0.5))_(0.5)In_(0.5)P. The first optical guide layer 224 a,the layered structure and the second optical guide layer 224 d aresuccessively stacked in bottom-to-top order.

There are considerations in determining the In, Ga and Al contents ineach layer 203 through 208 of the infrared laser device A and each layer223 through 228 of the red laser device B. These considerations are thateach layer is substantially equivalent in lattice constant to thesubstrate 201, the n-type cladding layer 203 and the first p-typecladding layer 205 have a larger band gap energy than the infraredactive layer 204, and the n-type cladding layer 223 and the first n-typecladding layer 225 have larger band gap energy than the infrared activelayer 224.

The method for manufacturing a semiconductor laser system according tothe second embodiment will be described hereinafter with reference toFIGS. 10A through 11B.

First, as shown in FIG. 10A, an n⁻type GaAs layer 202A, an n⁻type(Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P layer 203A, an undoped layeredstructure 204A, a p⁻type (Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P layer 205A, ap⁻type Ga_(0.5)In_(0.5)P layer 206A, a p⁻type(Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P layer 207A, a p⁻type Ga_(0.5)In_(0.5)Player 208A, and a p⁻type GaAs layer 212A are successively grown on asubstrate 201 of n⁻type GaAs by MOCVD, thereby forming an infrareddouble-heterojunction structure. The growth of the infrareddouble-heterojunction structure using MOCVD is continuously carried outby switching the source gas in the same reactor.

Next, the region of the infrared double-heterojunction structure to beformed with the red semiconductor laser device B is removed by etchinguntil it reaches the substrate 201. In this way, as shown in FIG. 10B, abuffer layer 202, an n-type cladding layer 203, an undoped infraredactive layer 204, a first p-type cladding layer 205, an etching stopperlayer 206, a second p-type cladding layer 207, a cap layer 208, and acap layer 212 are formed on the substrate 201.

The reason why the infrared double-heterojunction structure is grownearlier than a red double-heterojunction structure is as follows. In thered double-heterojunction structure, a material containing P, forexample, GaInP or AlGaInP, is used also for a red active layer. In filmsmade of these materials, the rate at which Zn is diffused under atemperature higher than 500° C. is ten or more times as fast as in thosemade of materials containing As, for example, GaAs or AlGaAs. Hence,when the red double-heterojunction structure is formed earlier, Zn isdiffused from the first and second p-type cladding layers 205 and 207 orthe like during the later crystal growth. As a result, the band gap andlasing wavelength vary. In other words, when the infrareddouble-heterojunction structure is grown earlier than the reddouble-heterojunction structure, this can prevent Zn from being diffusedinto the multi-quantum well layer constituting the red active layer.

Since in the second embodiment the first and second optical guide layers204 a and 204 d each have a thickness of 10 nm or more in the infrareddouble-heterojunction structure, this can more noticeably prevent Znfrom being diffused into the multi-quantum well layer.

Next, as shown in FIG. 10C, an n⁻type GaAs layer 222A, an n⁻type(Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P layer 223A, an undoped red activelayer 224A, a p⁻type (Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P layer 225A, ap⁻type Ga_(0.5)In_(0.5)P layer 226A, and a p⁻type(Al_(0.3)Ga_(0.7))_(0.5)In_(0.5)P layer 227A, a p⁻type Ga_(0.5)In_(0.5)Player 228A, and a p⁻type GaAs layer 232A are successively grown on thesubstrate 201 including the patterned infrared double-heterojunctionstructure by MOCVD, thereby forming a red double-heterojunctionstructure. The growth of the red double-heterojunction structure usingMOCVD is continuously carried out by switching the source gas in thesame reactor.

Next, the region of the red double-heterojunction structure formed onthe infrared double-heterojunction structure, the cap layer 212, thep⁻type GaAs layer 232A, and the region of the red double-heterojunctionstructure to be formed with an isolation trench C are removed byetching. In this way, as shown in FIG. 11A, the infrareddouble-heterojunction structure (referred to as infrared DH in thisfigure) and the red double-heterojunction structure (referred to as redDH in this figure) are formed on the substrate 201. The infrareddouble-heterojunction structure is composed of the buffer layer 202, then-type cladding layer 203, the undoped infrared active layer 204, thefirst p-type cladding layer 205, the etching stopper layer 206, thesecond p⁻type cladding layer 207, and the cap layer 208. The reddouble-heterojunction structure is composed of a buffer layer 222, ann-type cladding layer 223, an undoped red active layer 224, a firstp-type cladding layer 225, an etching stopper layer 226, a second p-typecladding layer 227, and a cap layer 228.

Next, an SiO₂ film is deposited on the infrared double-heterojunctionstructure and the red double-heterojunction structure. Thereafter, asshown in FIG. 11B, a stripe-shaped first mask pattern 235A and astripe-shaped second mask pattern 235B both made of a SiO₂ film areformed, by lithography and etching, on the predetermined regions of theinfrared double-heterojunction structure and the reddouble-heterojunction structure, respectively.

Next, the second p-type cladding layer 207 and the cap layer 208 bothconstituting the infrared double-heterojunction structure are etchedusing the first mask pattern 235A as a mask until this etching reachesthe etching stopper film 206. In this way, a stripe-shaped-ridge-likesecond p-type cladding layer 207 and a stripe-shaped cap layer 208 areformed on the infrared double-heterojunction structure. The secondp-type cladding layer 227 and the cap layer 228 both constituting thered double-heterojunction structure are etched using the second maskpattern 235B as a mask until this etching reaches the etching stopperfilm 226. In this way, a stripe-shaped-ridge-like second p-type claddinglayer 227 and a stripe-shaped cap layer 228 are formed on the reddouble-heterojunction structure.

In the second embodiment, the second p-type cladding layer 207 and thecap layer 208 in the infrared double-heterojunction structure have thesame compositions as the second p-type cladding layer 227 and the caplayer 228 in the red double-heterojunction structure, respectively.Therefore, the stripe-shaped second p-type cladding layers 207 and 227and the cap layers 208 and 228 can be formed by one etching processstep. This can reduce the number of process steps.

Next, as shown in FIG. 11C, a current blocking layer 209 made of n⁻typeAl_(0.5)In_(0.5)P is grown on the infrared double-heterojunctionstructure by MOCVD, and a current blocking layer 229 made of n⁻typeAl_(0.5)In_(0.5)P is grown on the red double-heterojunction structure.In this case, the current blocking layers 209 and 229 are formed by thesame crystal growth process step. An n⁻type Al_(0.5)In_(0.5)P layer doesnot grow on the first and second mask patterns 235A and 235B made of aSiO₂ film.

Next, after the removal of the first and second mask patterns 235A and235B, a contact layer 210 made of p⁻type GaAs and a contact layer 230made of p⁻type GaAs are grown by MOCVD on the infrareddouble-heterojunction structure and the red double-heterojunctionstructure, respectively. Thereafter, an n⁻type Al_(0.5)In_(0.5)P layerand a p⁻type GaAs layer are removed which have been grown inside theisolation trench C. In this way, an infrared semiconductor laser deviceA and a red semiconductor laser device B are formed on the substrate201.

Next, a metal film is deposited on the top surfaces of the infraredsemiconductor laser device A and the red semiconductor laser device B,and thereafter the metal film is patterned to from p-side electrodes 211and 231 (see FIG. 8). Next, a metal film is deposited on the bottomsurface of the infrared semiconductor laser device A and the redsemiconductor laser device B, and thereafter the metal film is patternedto form an n-side electrode 215 (see FIG. 8).

According to the method for manufacturing a semiconductor laser systemof the second embodiment, the stripe-shaped second p-type cladding layer207 and the cap layer 208 of the infrared double-heterojunctionstructure can be formed simultaneously with the stripe-shaped secondp-type cladding layer 227 and the cap layer 228 of the reddouble-heterojunction structure. In addition, the current blocking layer209 and the contact layer 210 of the infrared double-heterojunctionstructure can be formed simultaneously with the current blocking layer229 and the contact layer 230 of the red double-heterojunctionstructure. Therefore, the number of process steps can be reduced.

More particularly, when in the monolithic two-wavelength semiconductorlaser system a material containing P is not used for the infraredsemiconductor laser device A, six crystal growth process steps arerequired. However, when a material containing P is used for the infraredsemiconductor laser device A as in the second embodiment, only fourcrystal growth process steps are required. This can reduce cost in amanufacturing process.

In the second embodiment, the orientation of the principal surface ofthe n⁻type GaAs substrate 201 is inclined about 10 degrees from (100) inthe [011] or [011] direction as in the first embodiment. The reason forthis is that a natural superlattice is restrained from growing duringthe growth of the AlGaInP layer and thus the AlGaInP layer can preciselybe controlled to have a desired composition.

In particular, this inclination is effective for the red semiconductorlaser device B in preventing the occurrence of abnormalities in the bandgap of the red active layer 224 to obtain the lasing wavelength asdesigned.

In the first and second embodiments, optical guide layers are placed inboth the upper and lower parts of the multi-quantum well structure.However, in terms of preventing the crystallinity of the multi-quantumwell structure from being degraded, an optical guide layer made of amaterial containing As need only be provided in at least the lower partof the multi-quantum well structure.

In the first and second embodiments, a layer contacting themulti-quantum well structure need not necessarily be an optical guidelayer.

In the second embodiment, the isolation trench C may be formed after theformation of the contact layers 210 and 230 made of p⁻type GaAs.Furthermore, it may be filled with an insulating film of an SiO₂ film ora low-dielectric-constant film. This ensures the insulation between theinfrared laser device A and the red laser device B and improves theirstrengths. Therefore, the possibilities that cleavages of the devicesoccur or cracks occur during the packaging of these devices are reduced.

In the second embodiment, etching for forming the ridge shape andetching for forming the isolation trench C may be either wet etching ordry etching.

In the second embodiment, for example, SiN_(x), instead of an SiO₂ film,may be used as the stripe-shaped first and second mask patterns 235A and235B, as long as the selectivity of the mask patterns to the lowersemiconductor layered structure is large enough.

(Embodiment 3)

An optical pickup module according to a third embodiment of the presentinvention will be described hereinafter with reference to FIG. 12.

The optical pickup module comprises a light source 1 composed of themonolithic two-wavelength semiconductor laser system according to thesecond embodiment. The light source 1 emits a red light beam with awavelength of a 650 nm band and an infrared light beam with a wavelengthof a 780 nm band.

The red light beam with a wavelength of a 650 nm band is used to recorddata in and reproduce data from a DVD. When data are reproduced from aDVD, a light beam emitted from the light source 1 is changed in itsdirection by a reflecting mirror 2. Thereafter, the light beam isconverged through a collimator lens 3 and an objective lens 4 onto therecording surface of a disk 5. Reflected light beams from the recordingsurface of the disk 5 are incident through the objective lens 4 and thecollimator lens 3 to a holographic element 6. The reflected light beamsare diverged by the holographic element 6 and are incident to aplurality of light-receiving elements 7 and 8. Focus/tracking errorsignals and reproduction signals in the reproduction of the DVD aredetected based on signals detected by the light-receiving elements 7 and8.

On the other hand, the infrared light beam with a wavelength of a 780 nmband is used to record data in and reproduce data from a CD. When dataare reproduced from a CD, a light beam emitted from the light source 1is changed in its direction by the reflecting mirror 2 as in the use ofthe red light beam. Thereafter, the light beam is converged through thecollimator lens 3 and the objective lens 4 onto the recording surface ofthe disk 5. Reflected light beams from the recording surface of the disk5 are incident through the objective lens 4 and the collimator lens 3 tothe holographic element 6. The reflected light beams are diverged by theholographic element 6 and are incident to the plurality oflight-receiving elements 7 and 8. The focus/tracking error signals andreproduction signals in the reproduction of the CD are detected based onsignals detected by the light-receiving elements 7 and 8.

Since in the third embodiment the semiconductor layer system serving asthe light source 1 is a monolithic two-wavelength semiconductor lasersystem, the distance between light emitting points can be shortened.Therefore, the pickup module can be reduced in size and its opticalsystems can be consolidated into one system. This can reduce the numberof optical system components, such as a lens, and cost.

Furthermore, since the semiconductor laser device emitting infraredlight has a double-heterojunction structure composed of cladding layersof a material containing P and an active layer of a material thatcontains As but does not substantially contain P, this improves thereliability of the two-wavelength semiconductor laser system. Therefore,the optical pickup module can have higher performance and higherreliability.

In the third embodiment, a diffraction grating may be additionallyprovided for dividing a light beam emitted from the semiconductor lasersystem into three beams. In this case, the use of a three-beam methodbecomes possible. Thus, data are favorably reproduced from CDs or thelike. A prism or a beam splitter may be used instead of the holographicelement 6.

The structure and layout of components are not particularly restrictiveas long as the optical pickup module can play its role successfully.

In the third embodiment, the semiconductor laser system of the secondembodiment is used as the light source 1. Alternatively, thesemiconductor laser device of the first embodiment alone may be used.

1. A semiconductor laser device comprising a cladding layer of a firstconductive type, an active layer and a cladding layer of a secondconductive type, said layers being stacked on a semiconductor substrateof the first conductive type in bottom-to-top order, wherein the activelayer comprises a layered structure composed of at least one pair of awell layer and a barrier layer, an upper semiconductor layer formed ontop of the layered structure, and a lower semiconductor layer formedbeneath the layered structure, the cladding layer of the firstconductive type and the cladding layer of the second conductive type aremade of a material containing phosphorus, and the at least one pair ofthe well layer and barrier layer and the lower semiconductor layer aremade of a material that contains arsenic but does not substantiallycontain phosphorus.
 2. The semiconductor laser device of claim 1,wherein the upper semiconductor layer is made of a material thatcontains arsenic but does not substantially contain phosphorus.
 3. Thesemiconductor laser device of claim 1, wherein the upper and lowersemiconductor layers are optical guide layers.
 4. The semiconductorlaser device of claim 3, wherein the band gap of each said optical guidelayer is equivalent to or larger than that of the well layer.
 5. Thesemiconductor laser device of claim 3, wherein the cladding layer of thefirst conductive type and the cladding layer of the second conductivetype are made of (Al_(x)Ga_(1−x))_(y)In_(1−y)P (where 0≦x≦1 and 0≦y≦1),and the optical guide layers are made of Al_(x)Ga_(1−x)As (where 0≦x≦1).6. The semiconductor laser device of claim 5, wherein the well layer ismade of Al_(x)Ga_(1−x)As (where 0≦x≦1), and the barrier layer is made ofAl_(x)Ga_(1−x)As (where 0≦x≦1).
 7. The semiconductor laser device ofclaim 5, wherein the well layer is made of Al_(x)Ga_(1−x)As (where0≦x≦0.2).
 8. The semiconductor laser device of claim 5, wherein theoptical guide layers are made of Al_(x)Ga_(1−x)As (where 0.4≦x≦1). 9.The semiconductor laser device of claim 3, wherein the optical guidelayers each have a thickness of 10 nm or more.
 10. A semiconductor lasersystem comprising a plurality of semiconductor laser devices foremitting light beams of different wavelengths, said plurality ofsemiconductor laser devices being formed on a single substrate, whereinat least one of the plurality of semiconductor laser devices comprises acladding layer of a first conductive type, an active layer and acladding layer of a second conductive type, said layers being stacked ona semiconductor substrate of the first conductive type in bottom-to-toporder, the active layer comprises a layered structure composed of atleast one pair of a well layer and a barrier layer, an uppersemiconductor layer formed on top of the layered structure, and a lowersemiconductor layer formed beneath the layered structure, the claddinglayer of the first conductive type and the cladding layer of the secondconductive type are made of a material containing phosphorus, and the atleast one pair of the well layer and barrier layer and the lowersemiconductor layer are made of a material that contains arsenic butdoes not substantially contain phosphorus.
 11. An optical pickup modulecomprising: a semiconductor laser device; and a light receiving unit forreceiving light reflected from a recording medium after being emittedfrom the semiconductor laser device, wherein the semiconductor laserdevice comprises a cladding layer of a first conductive type, an activelayer and a cladding layer of a second conductive type, said layersbeing stacked on a semiconductor substrate of the first conductive typein bottom-to-top order, the active layer comprises a layered structurecomposed of at least one pair of a well layer and a barrier layer, anupper semiconductor layer formed on top of the layered structure, and alower semiconductor layer formed beneath the layered structure, thecladding layer of the first conductive type and the cladding layer ofthe second conductive type are made of a material containing phosphorus,and the at least one pair of the well layer and barrier layer and thelower semiconductor layer are made of a material that contains arsenicbut does not substantially contain phosphorus.
 12. An optical pickupmodule comprising: a semiconductor laser system; and a light receivingunit for receiving light reflected from a recording medium after beingemitted from the semiconductor laser system, wherein the semiconductorlaser system comprises a plurality of semiconductor laser devices foremitting light beams of different wavelengths, said plurality ofsemiconductor laser devices being formed on a single substrate, at leastone of the plurality of semiconductor laser devices comprises a claddinglayer of a first conductive type, an active layer and a cladding layerof a second conductive type, said layers being stacked on asemiconductor substrate of the first conductive type in bottom-to-toporder, the active layer comprises a layered structure composed of atleast one pair of a well layer and a barrier layer, an uppersemiconductor layer formed on top of the layered structure, and a lowersemiconductor layer formed beneath the layered structure, the claddinglayer of the first conductive type and the cladding layer of the secondconductive type are made of a material containing phosphorus, and the atleast one pair of the well layer and barrier layer and the lowersemiconductor layer are made of a material that contains arsenic butdoes not substantially contain phosphorus.
 13. A method formanufacturing a semiconductor laser system, comprising the steps of:forming a first double-heterojunction structure on a semiconductorsubstrate; removing a predetermined region of the firstdouble-heterojunction structure to form a first semiconductor laserdevice of the remaining first double-heterojunction structure; forming asecond double-heterojunction structure on the semiconductor substrateincluding the top surface of the remaining first double-heterojunctionstructure; and removing a region of the second double-heterojunctionstructure located on the remaining first double-heterojunction structureto form a second semiconductor laser device of the remaining seconddouble-heterojunction structure, wherein the step of forming a firstdouble-heterojunction structure comprises the steps of: forming a firstcladding layer made of a material containing phosphorus on thesemiconductor substrate; forming, on the first cladding layer, a lowersemiconductor layer made of a material that contains arsenic but doesnot substantially contain phosphorus, then forming, on the lowersemiconductor layer, a layered structure made of a material thatcontains arsenic but does not substantially contain phosphorus andcomposed of at least one pair of a well layer and a barrier layer, andthen forming an upper semiconductor layer on the layered structure,thereby forming a first active layer composed of the lower semiconductorlayer, the layered structure and the upper semiconductor layer; andforming, on the first active layer, a second cladding layer made of amaterial containing phosphorus, and the step of forming a seconddouble-heteroj unction structure comprises the steps of: forming a thirdcladding layer made of a material containing phosphorus on thesemiconductor substrate including the top surface of the firstsemiconductor laser device; forming a second active layer on the thirdcladding layer; and forming a fourth cladding layer on the second activelayer.
 14. The method for manufacturing for a semiconductor laser systemof claim 13, wherein the step of forming a first double-heterojunctionstructure comprises the step of continuously growing the first claddinglayer, the first active layer and the second cladding layer.